BS 1748-8-1960 铜合金分析方法.第8部分铜合金中磷的测定方法(光度测量法) .pdf
《BS 1748-8-1960 铜合金分析方法.第8部分铜合金中磷的测定方法(光度测量法) .pdf》由会员分享,可在线阅读,更多相关《BS 1748-8-1960 铜合金分析方法.第8部分铜合金中磷的测定方法(光度测量法) .pdf(8页珍藏版)》请在三一文库上搜索。
1、BRITISH STANDARD BS 1748-8: 1960 Method for The determination of phosphorus in copper alloys (photometric method) BS 1748-8:1960 This British Standard, having been approved by the Non-ferrous Metals Industry Standards Committee and endorsed by the Chairman of the Engineering Divisional Council, was
2、published under the authority of the General Council on 20 July 1960 BSI 11-1999 The following BSI references relate to the work on this standard: Committee reference NFE/-/2 Draft for comment CZ(NFE) 8591 ISBN 0 580 01819 9 Co-operating organizations The Non-ferrous Metals Industry Standards Commit
3、tee, under whose supervision this British Standard was prepared, consists of representatives from the following Government departments, and scientific and industrial organizations: Admiralty*Institution of Mechanical Engineers Aluminium Development Association(Automobile Division) Aluminium Industry
4、 CouncilInstitution of Mining and Metallurgy Association of Bronze and Brass Founders*Institution of Structural Engineers Association of Consulting Engineers,Lead Development Association IncorporatedLead Sheet and Pipe Manufacturers Association of Non-ferrous Metal StockistsFederation British Bronze
5、 and Brass IngotLight Metal Founders Association Manufacturers Association*London Metal Exchange British Electrical and Allied ManufacturersMagnesium Industry Council AssociationMinistry of Aviation* British Non-ferrous Metals FederationNational Brassfoundry Association British Non-ferrous Metals Re
6、searchPost Office Association*Royal Institute of British Architects Cable Makers AssociationSociety of British Aircraft Constructors Copper Development AssociationSociety of Motor Manufacturers and Traders Crown Agents for Oversea Governments andLimited AdministrationsTin Research Institute High Com
7、mission of IndiaWar Office High Conductivity Copper AssociationZinc Development Association Institute of British FoundrymenIndividual manufacturers Institute of Metals The Government departments and scientific and industrial organizations marked with an asterisk in the above list, together with the
8、following, were directly represented on the sub-committee entrusted with the preparation of this British Standard: D.S.I.R. Laboratory of the GovernmentIndividual firms Chemist Amendments issued since publication Amd. No.DateComments BS 1748-8:1960 BSI 11-1999i Contents Page Co-operating organizatio
9、nsInside front cover Forewordii Introduction1 Apparatus1 Solutions required1 Sampling1 Calibration2 Procedure2 BS 1748-8:1960 ii BSI 11-1999 Foreword This standard makes reference to the following British Standards: BS 1400, Copper alloy ingots and castings. BS 1499, Sampling non-ferrous metals. Thi
10、s method for the determination of phosphorus is one of a series of methods for the analysis of copper alloys, which will form a complete British Standard issued in several parts. The methods are intended primarily for the analysis of the copper alloys included in BS 1400, “Copper alloy ingots and ca
11、stings”, and those being included in the series of schedules of wrought copper and copper alloys, BS 2870 to BS 2875, of which BS 2871 has already been published, and the remainder are in course of preparation. The methods have been found to give reliable and reproducible results and, while in some
12、instances they may appear to be lengthy, it should be realized that they are put forward as referee methods to be used in cases of dispute. In the preparation of the calibration graphs an attempt has been made to define concentrations, but because these are linked with the particular instrument used
13、 for determining optical density they should be used only as a guide. A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immu
14、nity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages 1 to 3 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on th
15、e inside front cover. BS 1748-8:1960 BSI 11-19991 Introduction a) Principle. The sample is dissolved in a mixture of nitric and hydrochloric acids, and phosphorus is converted into orthophosphoric acid. Phosphovanadomolybdic acid is subsequently formed and the yellow colour is measured photometrical
16、ly. b) Range. Up to 1.20 per cent phosphorus. c) Reproducibility. Experiments have been carried out independently by a number of analysts using the method recommended in this standard. The degree of reproducibility that can be expected is shown by the following analysis of the results obtained: d) A
17、pplication. The method is applicable to all types of copper alloys provided a suitable compensating solution is used when elements are present which would otherwise interfere in the optical density determination. The percentage of arsenic normally present in the specified alloys does not interfere.
18、Apparatus a) Grade A graduated glassware shall be used throughout. b) Any instrument suitable for measuring the optical density of the solution at a wave-length of 435 mX may be used. If a filter photometer is used the filter combination should conform as closely as possible to the above wave-length
19、. The following conditions have been found suitable: Ilford 601 with Chance H503. 4 cm and 1 cm cells. Solutions required All reagents shall be of the highest purity obtainable, and distilled water shall be used throughout. Solutions shall be freshly prepared and, where necessary, filtered. Standard
20、 potassium dihydrogen phosphate (1 ml 0.20 mg of phosphorus). Dissolve 0.8787 g of potassium dihydrogen phosphate (previously dried at 105 pC) in about 250 ml of water. Add 100 ml of nitric acid (20 per cent v/v) and dilute to 1 litre in a graduated flask. Ammonium molybdate (10 per cent w/v). Disso
21、lve 100 g of ammonium molybdate (NH4)6Mo7O244H2O) in about 600 ml of warm water, cool, and dilute to 1 litre. Filter through a fine textured paper immediately before using. Ammonium vanadate (0.25 per cent w/v). Dissolve 2.5 g of ammonium metavanadate in about 500 ml of hot water. Add 20 ml of nitri
22、c acid (50 per cent v/v), cool, and dilute to 1 litre. Hydrogen peroxide (3 per cent). Dilute 10 ml of hydrogen peroxide (100 vol) to 100 ml. Store in a dark bottle in a cool place. Nitric acid (50 per cent v/v). Dilute 50 ml of nitric acid (sp. gr. 1.42) to 100 ml. Nitric acid (20 per cent v/v). Di
23、lute 20 ml of nitric acid (sp. gr. 1.42) to 100 ml. Nitric-hydrochloric acid mixture. To 500 ml of water add 320 ml of nitric acid (sp. gr. 1.42) and 120 ml of hydrochloric acid (sp. gr. 1.161.18). Cool and dilute to 1 litre. Sampling Recommended methods of obtaining a suitable sample for the analyt
24、ical procedure given below are described in BS 1499, “Sampling non-ferrous metals”. Phosphorus contentStandard deviation per cent Below 0.10 0.5 1.20 per cent 0.004 0.01 0.02 BS 1748-8:1960 2 BSI 11-1999 Calibration Weigh 2.00 g of pure copper (containing less than 0.0002 per cent phosphorus) into e
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- BS 1748-8-1960 铜合金分析方法.第8部分铜合金中磷的测定方法光度测量法 1748 1960 铜合金 分析 方法 部分 测定 光度 测量
链接地址:https://www.31doc.com/p-3646497.html