《BS-EN-1842-1997.pdf》由会员分享,可在线阅读,更多相关《BS-EN-1842-1997.pdf(8页珍藏版)》请在三一文库上搜索。
1、| | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BRITISH STANDARD BS EN 1842 : 1997 The Eur
2、opean Standard EN 1842 : 1997 has the status of a British Standard ICS 83.080.10 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW Plastics Thermoset moulding compounds (SMC - BMC) Determination of compression moulding shrinkage Licensed Copy: sheffieldun sheffieldun, na, Mon Oc
3、t 30 05:36:48 GMT+00:00 2006, Uncontrolled Copy, (c) BSI This British Standard, having been prepared under the direction of the Sector Board for Materials and Chemicals, was published under the authority of the Standards Board and comes into effect on 15 November 1997 BSI 1997 ISBN 0 580 28664 9 BS
4、EN 1842 : 1997 Amendments issued since publication Amd. No.DateText affected National foreword This British Standard is the English language version of EN 1842 : 1997. It is also for use for the revision or amendment of other national standards as practicable, but it should not be presumed to apply
5、to any existing standard or specification which contains or makes reference to a different test method until that standard/specification has been amended or revised to make reference to this method and adjust any requirements as appropriate. Attention is drawn to the existence of BS 2782 : Methods o
6、f testing plastics. Part 6 : Dimensional properties. Method 640A : 1979 Determination of shrinkage of test specimens in the form of bars of compression moulded thermosetting moulding materials, which is identical to and dual numbered with ISO 2577. The text of ISO 2577 : 1975 was used as the basis f
7、or the preparation of this European Standard. The UK participation in its preparation was entrusted to Technical Committee PRI/42, Fibre reinforced thermo-setting plastics and prepregs, which has the responsibility to: aid enquirers to understand the text; present to the responsible European committ
8、ee any enquiries on the interpretation, or proposals for change, and keep the UK interests informed; monitor related international and European developments and promulgate them in the UK. A list of organizations represented on this committee can be obtained on request to its secretary. Cross-referen
9、ces The British Standards which implement international or European publications referred to in this document may be found in the BSI Standards Catalogue under the section entitled International Standards Correspondence Index, or by using the Find facility of the BSI Standards Electronic Catalogue.
10、Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, the EN title page, pages 2 to 4, an inside back cover and a back cover. Licensed Copy: sheffieldun sheffieldun, na, Mon Oct 30
11、05:36:48 GMT+00:00 2006, Uncontrolled Copy, (c) BSI CEN European Committee for Standardization Comite Europe en de Normalisation Europa isches Komitee fu r Normung Central Secretariat: rue de Stassart 36, B-1050 Brussels 1997 CEN All rights of exploitation in any form and by any means reserved world
12、wide for CEN national Members. Ref. No. EN 1842 : 1997 E EUROPEAN STANDARDEN 1842 NORME EUROPE ENNE EUROPA ISCHE NORM July 1997 ICS 83.080.10 Descriptors: Plastics, thermosetting resins, plastic moulding, compression moulding, tests, determination, shrinkage English version Plastics Thermoset mouldi
13、ng compounds (SMC - BMC) Determination of compression moulding shrinkage Plastiques Matie res a mouler thermodurcissables (SMC - BMC) De termination du retrait au moulage par compression Kunststoffe Wa rmeha rtende Formmassen (SMC - BMC) Bestimmungen der Verarbeitungsschwindung This European Standar
14、d was approved by CEN on 1997-06-29. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such na
15、tional standards may be obtained on application to the Central Secretariat or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and
16、notified to the Central Secretariat has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerla
17、nd and United Kingdom. Licensed Copy: sheffieldun sheffieldun, na, Mon Oct 30 05:36:48 GMT+00:00 2006, Uncontrolled Copy, (c) BSI Page 2 EN 1842 : 1997 BSI 1997 Foreword This European Standard has been prepared by Technical Committee CEN/TC 249, Plastics, the secretariat of which is held by IBN. Thi
18、s European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by January 1998, and conflicting national standards shall be withdrawn at the latest by January 1998. According to the CEN/CENELEC Internal Regulations, t
19、he national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kin
20、gdom. Contents Page Foreword2 1Scope3 2Normative references3 3Definitions3 4Apparatus3 5Sampling and conditioning of the moulding compound 3 6Test specimens3 7Procedure3 8Expression of results4 9Test report4 10Precision4 Licensed Copy: sheffieldun sheffieldun, na, Mon Oct 30 05:36:48 GMT+00:00 2006,
21、 Uncontrolled Copy, (c) BSI Page 3 EN 1842 : 1997 BSI 1997 1 Scope This European Standard specifies a method to determine the moulding shrinkage of compression moulded test specimens of thermoset moulding compounds. It applies only to materials which exhibit no post-shrinkage after moulding such as
22、polyester SMC (sheet moulding compound) and BMC (bulk moulding compound). Knowledge of the shrinkage allows the construction of moulds to produce parts with accurate dimensions, as well as evaluation of the suitability of a moulding compound for this purpose. 2 Normative references This European Sta
23、ndard incorporates, by dated or undated reference, provisions from other publications. These normative references are cited at the appropriate places in the text and the publications are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply
24、to this European Standard only when incorporated in it by amendment or revision. For undated references the latest edition of the publication referred to applies. ISO 291 : 1977Plastics Standard atmospheres for conditioning and testing ISO 472 : 1988Plastics Vocabulary ISO 2577 : 1984Plastics Thermo
25、setting moulding materials Determination of shrinkage EN ISO 12114Fibre reinforced plastics Thermosetting moulding compounds and prepregs Determination of cure characteristics (ISO 12114 : 1997) prEN 12576Plastics Fibre reinforced composites Preparation of compression moulded test plates of SMC, BMC
26、 and DMC 3 Definitions For the purposes of this standard, the definitions of ISO 472 : 1988 and the following definition apply: moulding shrinkage the difference in dimensions between a moulding and the mould cavity in which it was moulded, both the mould and the moulding being at normal temperature
27、 when measured (ISO 2577 : 1984). 4 Apparatus 4.1 Mould and press suitable for moulding the test specimens specified in clause 6. Use a mould with a plane mould cavity not smaller than 200 cm2. This mould shall be used with punch and die being able to maintain a positive pressure on the material. It
28、 can be rectangular, square or circular or as described in EN ISO 12114 or in prEN 12576. The mould can be designed with gauge marks engraved into mould cavity near opposite ends and with or without draft angles. NOTE. Draft angles result in the opposite ends not being parallel which can cause diffi
29、culties in length measurement (see 7.4). In this case a reference plane at points 2 mm above the smaller surface can be used. 4.2 Equipment suitable for measuring the sizes of test specimens and the corresponding cavity of the mould with an accuracy of 0,01 mm. 4.3 Non metallic cooling rack to hold
30、the test specimens vertically with a minimum spacing of 20 mm. NOTE. To achieve symmetrical cooling, both outer test specimens are protected by additional protective plates. 5 Sampling and conditioning of the moulding compound Samples shall be taken from the moulding compound after maturation within
31、 the shelf-life given in the specification. They shall be placed inside an appropriate bag to avoid loss of volatile components and moisture absorption, kept under standard atmosphere (according to ISO 291 : 1997) until equilibrium is reached and then moulded into test specimens. 6 Test specimens Te
32、st specimens are mouldings obtained by using mould and press (see 4.1). The thickness shall be between 3,5 mm and 5,5 mm. 7 Procedure 7.1 Measure the length of the mould cavity (see note in 4.1), or the distance between the engraved gauge marks in the mould cavity to the nearest 0,01 mm at standard
33、atmosphere as reference length L0. Record this measurement for use in the calculation of shrinkage. NOTE. Every year it is recommended to check mould dimensions for wear. Licensed Copy: sheffieldun sheffieldun, na, Mon Oct 30 05:36:48 GMT+00:00 2006, Uncontrolled Copy, (c) BSI Page 4 EN 1842 : 1997
34、BSI 1997 7.2 Mould three specimens. Unless other conditions are specified or agreed between user and supplier the following conditions apply: mould temperature: 140 C1 % ; mould coverage: not less than 90 % for SMC. Moulding compounds like BMC shall be preformed to a homogeneous charge prior to moul
35、ding; moulding pressure: 7 MPa5 % ; Pressing time: 40 seconds per millimetre of thickness of moulded test specimen or for whatever longer time is necessary to ensure full cure. The mould shall be closed within 15 s after charging. On the moulded SMC test specimens, identify the production direction
36、and/or unidirectional reinforcement direction if applicable. 7.3 After removal from the mould, allow the test specimens to cool down to room temperature by placing them in the cooling rack (see 4.3). Store them at standard atmosphere for a minimum of 16 h, or for a shorter time providing it has been
37、 shown that it gives the same results. 7.4 For the determination of moulding shrinkage, measure at standard atmosphere, to the nearest 0,01 mm, the length of the test specimens between opposite ends as L1. With engraved gauge marks, measure the distance between the marks. With draft angles at the en
38、ds of the test specimens, measure the length of the reference plane (see note in 4.1). Without draft angles, measure at any height the distance between opposite ends. Carry out one measurement per test specimen. 8 Expression of results The moulding shrinkage MS is given, as a percentage, by the form
39、ula: MS =3 100 L02 L1 L0 where L0is the reference length of the mould, in millimetres, determined as in 7.1; L1is the corresponding length of the test specimen in millimetres, according to 7.4. NOTE. A positive value (L02 L1 0) indicates a shrinkage of the material and a negative value (L02 L1 0) an
40、 expansion. 9 Test report The test report shall include the following particulars: a) reference to this European Standard; b) the type and designation of the moulding compound; c) the type and size of mould used; d) the thickness and the moulding conditions: temperature, pressure, pressing time; e)
41、the moulding shrinkage, MS, as a percentage, stating the individual values and the average value. In case of SMC, specify the direction of measurements with respect to the direction of the SMC machine; and/or to the direction of the unidirectional reinforcement; f) the date of the tests. 10 Precisio
42、n The precision of this method is not known because interlaboratory data are not available. When interlaboratory data are obtained, a precision statement will be added with the next revision. Licensed Copy: sheffieldun sheffieldun, na, Mon Oct 30 05:36:48 GMT+00:00 2006, Uncontrolled Copy, (c) BSI b
43、lank Licensed Copy: sheffieldun sheffieldun, na, Mon Oct 30 05:36:48 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BSI 389 Chiswick High Road London W4 4AL | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |
44、 | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level
45、. It is incorporated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be gra
46、teful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: 020 8996 9000. Fax: 020 8996 7400. BSI offers members an individual updating serv
47、ice called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: 020 8996 9001. Fax: 020 8996 7001. In response to orders for int
48、ernational standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standards through its Library and its
49、Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: 020 8996 7111. Fax: 020 8996 7048. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: 020 8996 7002. Fax: 020 8996 7001. Copyright Copyright subsists i