1、BRITISH STANDARD BS EN 61249-7-1:1996 IEC 1249-7-1: 1995 Materials for interconnection structures Part 7: Sectional specification set for restraining core materials Section 1: Copper/invar/copper The European Standard EN 61249-7-1:1995 has the status of a British Standard ICS 31.180 Licensed Copy: s
2、heffieldun sheffieldun, na, Fri Nov 10 16:31:52 GMT+00:00 2006, Uncontrolled Copy, (c) BSI BS EN 61249-7-1:1996 This British Standard, having been prepared under the direction of the Electrotechnical Sector Board, was published under the authority of the Standards Board and comes into effect on 15 A
3、ugust 1996 BSI 11-1999 The following BSI references relate to the work on this standard: Committee reference EPL/52 Draft announced in BSI News Update May 1996 ISBN 0 580 26031 3 Committees responsible for this British Standard The preparation of this British Standard was entrusted to Technical Comm
4、ittee EPL/52, Printed circuits, on which the following bodies were represented: British Telecommunications plc Electrical and Electronic Industries Association (BEAMA Ltd.) Federation of the Electronics Industries GAMBICA (BEAMA Ltd.) Institute of Metal Finishing National Supervisory Inspectorate Pr
5、inted Circuit Interconnection Federation Surface Mount CIC type B Copper/Invar/copper in the ratio 12,5/75/12,5 by volume percentage; CIC type C Copper/Invar/copper in the ratio 20/60/20 by volume percentage. The tolerance shall be 10 % of the nominal content of each component. 3.2 Constituent mater
6、ials 3.2.1 Invar Nickel-iron alloy of the following composition: 3.2.2 Copper The copper shall have a minimum purity of 99,8 % copper (with silver content regarded as copper), excluding any “as shipped” surface treatment. Element% by weight Nickel35,5 36,5 Phosphorus0,025 maximum Sulphur0,025 maximu
7、m Carbon0,12 maximum Manganese0,50 maximum Silicon0,25 maximum Ironbalance Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 10 16:31:52 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 61249-7-1:1995 4 BSI 11-1999 4 Electrical properties Table 1 Electrical properties 5 Non-electrical properties 5.1
8、Appearance The copper-clad faces shall be free from oxide, blisters, wrinkles, pin-holes, deep scratches, and pits. 5.2 Thickness The thickness of the CIC material, measured by a micrometer, shall not depart from the nominal thickness by more than the appropriate value shown below. Table 2 Thickness
9、 tolerances 5.3 Bow and twist Table 3 Bow and twist 5.4 Tensile strength and elongation Table 4 Tensile and elongation properties PropertyTest methodCIC typeRequirement M7m ResistivityAs specified in IEC 468 A0,17 0,01 B0,07 0,01 C0,04 0,01 Nominal thickness mm Tolerance mm 0,10 to 0,300,010 Over 0,
10、30 to 0,600,025 Over 0,60 to 1,200,050 Over 1,20 to 2,400,10 Property Test method (sub-clause of IEC 249-1) Requirement For all CIC types % Bow3.10,5 max. Twist3.30,5 max. PropertyTest methodCIC typeRequirement Tensile strengthAs specified in ISO 6892A380 N/mm2 to 480 N/mm2 B380 N/mm2 to 480 N/mm2 C
11、310 N/mm2 to 480 N/mm2 Elongation (gauge length: 50 mm) As specified in ISO 6892A25 % min. B20 % min. C20 % min. Licensed Copy: sheffieldun sheffieldun, na, Fri Nov 10 16:31:52 GMT+00:00 2006, Uncontrolled Copy, (c) BSI EN 61249-7-1:1995 BSI 11-19995 5.5 Modulus of elasticity Table 5 Modulus of elas
12、ticity 5.6 Thermal coefficient of expansion Table 6 Thermal coefficient of expansion 5.7 Bond strength between copper and Invar The CIC material shall be capable of being bent 180 around an arbor with a diameter equal to the thickness of the material without showing separation between the layers, at
13、 room temperature. 6 Surface treatment The sheet shall be capable of being bonded to a laminate according to the suppliers recommendations. If agreed upon between purchaser and supplier, the copper surface may be given a chemical or electrochemical treatment to enhance adhesion to the required subst
14、rate. If such a treatment has been applied, it shall be substantially uniform in colour and intensity over the entire area of the surface so treated, and shall be sufficiently adherent to withstand normal handling of the material during the users manufacturing processes, including the lamination pro
15、cess itself, and to meet the relevant requirements of the laminate manufactured from the CIC material. 7 Packaging and marking The material shall be packed adequately to avoid damage, bow, contamination in transit and storage. Separate sheets shall be interleaved with chemically neutral, or suitably
16、 treated paper. Each package shall be labelled with the material type designation, the manufacturers name, the nominal material thickness and the batch reference number. The package label shall also show the number of sheets. Any labels on sheets shall remain securely fixed during normal handling bu
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- BS-EN-61249-7-1-1996 IEC-61249-7-1-1995 BS EN 61249 1996 IEC 1995
链接地址:https://www.31doc.com/p-3745244.html