1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2006 10 12 N-STATUS Replaced by WSS-M4D952-A2 2005 05 26 Revised Inserted 3.0; Deleted 3.1, 3.4 parts subjected to this test are not expected to remain within design tolerances and therefore shall not be used in assembly production. Complianc
2、e with test requirements indicates optimal molding parameters. Test Method: Unassembled parts shall be subjected to a 30 min exposure in a mechanical convection oven preheated and maintained at 121 C. Parts shall be supported by an oven shelf, and positioned with maximum surface contact to the oven
3、shelf. Nonlinear shrinkage occurs in curved lengths; consequently, shrinkage should always be determined from sections. Part shall be examined after cooling to room temperature (23 +/- 2 C). 3.3.2 Environmental Cycling There shall be no change in appearance, color, or configuration after exposing th
4、e part for 5 cycles, each cycle consisting of: ENGINEERING MATERIAL SPECIFICATION ESB-M4D383-A1/A2 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 3 of 3 . 4 h at 88 C . 4 h at 38 C and 100% relative humidity . 16 h at -40 C . 4 h at 38 C and 100% relative humidity
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- FORD ESB M4D383 A2 2006
链接地址:https://www.31doc.com/p-3755410.html