FORD-WSK-M4D647-A-2006.pdf
《FORD-WSK-M4D647-A-2006.pdf》由会员分享,可在线阅读,更多相关《FORD-WSK-M4D647-A-2006.pdf(4页珍藏版)》请在三一文库上搜索。
1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2006 04 28 N-STATUS Replaced by WSK-M4D648-A A. Reaume/M. Masserant 2005 10 17 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.7, 3.8 & 4 1989 05 19 SM/EQ9548 TP Released M. Siewert Printed copies are uncontrolled Copyright 2006, Ford Global Techno
2、logies, LLC Page 1 of 4 POLYAMIDE (PA) 66 MOLDING COMPOUND WSK-M4D647-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a polyamide 66 molding compound. 2. APPLICATION This specification was released originally for material used for retainer guides. NOTICE: This
3、material absorbs and retains moisture. Part design and tolerances must accommodate changes in part dimensions and physical properties due to moisture absorption or loss in the service/assembly environment. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification o
4、f materials. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 CONDITIONING AND TEST CONDITIONS All test values indicated herein are based on material conditioned
5、in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5% relative humidity for not less than 24 h prior to testing and tested under the same conditions unless otherwise specified. All test materials immediately after processing have to be sealed in containers that are impermeable to water vapor. If th
6、e moisture content exceeds 0.2%, condition the material for a minimum of 16 h at 40 - 50 C at a reduced pressure below 133 Pa. Conduct tests in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5% relative humidity. Individual specimens shall not be removed from closed containers until immediately be
7、fore testing. 3.4 MOLDING COMPOUND 3.4.1 Melt Temperature 250 - 265 C (ISO 1218, Method B/ASTM D 789) 3.5 MOLDED TEST SPECIMEN 3.5.1 Preparation of Test Specimens Unless otherwise specified all tests shall be carried out on injection molded one-end gated test specimens. ENGINEERING MATERIAL SPECIFIC
8、ATION WSK-M4D647-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 4 The following dimensions are required: A. 150 min x 10 x 4.0 +/- 0.2 mm (Tensile Bar, ISO 3167) B. 120 x 10 x 4.0 +/- 0.2 mm Specimens with shorter dimensions shall be cut from the center por
9、tion of the test specimen A and/or B. The specimens shall be prepared according to ISO 294. No annealing allowed. 3.5.2 Density 1.12 - 1.16 g/cm3 (ISO 1183, Method A/ASTM D 792, Method A1) 3.5.3 Tensile Strength at Yield, min 70 MPa (ISO R 527/ASTM D 638M, 150 x 10 x 4.0 +/- 0.2 mm specimen, 50 mm/m
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- FORD WSK M4D647 2006
链接地址:https://www.31doc.com/p-3756242.html