FORD-ESB-M6J142-A-2008.pdf
《FORD-ESB-M6J142-A-2008.pdf》由会员分享,可在线阅读,更多相关《FORD-ESB-M6J142-A-2008.pdf(3页珍藏版)》请在三一文库上搜索。
1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2008 04 29 Revised Inserted 3.0; Deleted 3.7 & 4 1981 04 10 Released PCE-0262/CEL1-CVL1-C5L1-1R-588820-1 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 3 PRIMER, FLASH - FOR POLYOLEFIN SUBSTRATES EXTER
2、IOR ESB-M6J142-A 1. SCOPE The material defined by this specification is a primer with good adhesion to polyolefin surfaces. The primer may be either clear or pigmented. 2. APPLICATION This specification was released originally for primers used as thin flash coats on exterior polyolefin copolymer par
3、ts, followed by a color coat. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COMPOSITION The non-volatile portion shall be composed of resins wi
4、th good adhesion to polyolefin copolymer and may be pigmented as a guide to visual coverage if desirable. The volatile portion shall be balanced to provide good application properties and complete surface wetting. The material shall be compatible as a flash primer with enamels or primer surfacers no
5、rmally used in production. The material shall not cause skin rash or irritation (dermatitis) to exposed handlers in normal production operations. 3.2 PHYSICAL PROPERTIES 3.2.1 Non-Volatile Solids (FLTM BI 102-01) Shall be established by the vendor on the initial approved production batch. Tolerance
6、shall be +/- 2.0%. 3.2.2 Viscosity (FLTM BI 111-01) Shall be established by the vendor on the initial approved production batch. Tolerance shall be +/- 5 s. 3.2.3 Stability The material shall not liver or jell and shall retain its normal application and working properties after 30 days shelf storage
7、 at 23 +/- 2 C. -,-,- ENGINEERING MATERIAL SPECIFICATION ESB-M6J142-A Copyright 2008, Ford Global Technologies, LLC Page 2 of 3 3.3 PREPARATION OF TEST PANELS 3.3.1 Substrate (see para 5.3) Conduct test on exterior grade low density polyolefin copolymer plaques or parts. 3.3.2 Surface Preparation Wi
8、pe plastic with M14J242 Toluene. 3.3.3 Primer Spray as received, without reduction, 1-2 passes completely wetting the panel (film thickness 0.1 mil (2.5 m) max). 3.3.4 Color Coat (see para 5.3) Apply 1.0 mil (26 m) min. 3.3.5 Aging After application of the color coat, all panels shall be aged 72 h m
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- FORD ESB M6J142 2008
链接地址:https://www.31doc.com/p-3757247.html