1、 ENGINEERING STANDARDS Material Specification Plastics GMP.E/P.122 Polyolefin Alloy - Weather Resistant, 1300 MPa Flexural Modulus, 20% Filled, High Flow Copyright 2006 General Motors Corporation All Rights Reserved December 2006 Originating Department: North American Engineering Standards Page 1 of
2、 3 1 Scope 1.1 Material Description. This specification covers the properties of a weather resistant, 1300 MPa nominal flexural modulus polyolefin alloy, 20% nominal mineral filler, high flow, pellet form, injection molding compound. For the purpose of this specification, polyolefin alloy is defined
3、 as an alloy of polypropylene plastic and EP or EPDM rubber. 1.1.1 Paintability Approved paint systems that can be used on this material are listed in the GM Approved Paint on Parts Systems (GM APOPS) database. 1.2 Symbols. The material abbreviation according to ISO 11469 is E/P. 1.3 Typical Applica
4、tions. Typical applications include the following: body side moldings, claddings, rockers, wheel flares. 2 References Note: Only the latest approved standards are applicable unless otherwise specified. 2.1 External Standards/Specifications. ASTM D3763 ISO 1183 ISO 178 ISO 3451-1 ISO 294 ISO 11469 IS
5、O 527-1 SAE J1545 ISO 527-2 SAE J1960 ISO 1133 2.2 GM Standards/Specifications. GM9327P GMW3059 GMW3001 GMW3221 3 Requirements Important physical, mechanical and thermal properties that characterize the material are summarized in charts. The color shall be specified on drawings, in material specific
6、ations and otherwise. 3.1 Requirements on Test Specimens. Unless otherwise specified, test specimens shall be injection molded according to ISO 294. Test shall be conducted 40 h minimum after molding and immediately following a conditioning period of 24 h minimum at conditions per GMW3221, code A. A
7、ll tests shall be performed on unannealed specimens. Tests shall be conducted using the latest issue of the test methods indicated. Suitable precautions should be taken to ensure that applicable safe limits are not exceeded when conducting test procedures, processes, and/or handling the materials re
8、quired by this specification. 3.2 Requirements on Parts. 3.2.1 Compound Properties. See Table 1. 3.2.2 Compound Properties. See Table 2. 4 Manufacturing Process Not Applicable. 5 Rules and Regulations 5.1 All materials supplied to this specification must comply with the requirements of GMW3001, Rule
9、s and Regulations for Material Specifications. 5.2 All materials supplied to this specification must comply with the requirements of GMW3059, Restricted and Reportable Substances for Parts. Copyright General Motors North America Provided by IHS under license with GM Licensee=IHS Employees/1111111001
10、, User=Japan, IHS Not for Resale, 06/23/2008 23:22:07 MDTNo reproduction or networking permitted without license from IHS -,-,- GMP.E/P.122 GM ENGINEERING STANDARDS Copyright 2006 General Motors Corporation All Rights Reserved Page 2 of 3 December 2006 Table 1: Compound Properties (Black or Natural)
11、 Properties Standard Unit Values Mineral Filler ISO 3451-1, Method A % by mass 17 to 21 Density ISO 1183, Method A g/cm 1.00 to 1.05 Melt Flow Rate ISO 1133 g/10 min. 22 to 28 Flexural Modulus ISO 178, 80 x 10 x 4 mm specimen, 2 mm/minute test speed, 64 mm support span MPa 1150 to 1500 Tensile Stres
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- GMNA GMP 122 2006
链接地址:https://www.31doc.com/p-3767496.html