1、 ENGINEERING STANDARDS Material Specification Plastics GMP.E/P.119 Polyolefin Alloy UV Stabilized, 20% Mineral Filler, Scratch Resistant, Injection Molded 1 Scope 1.1 Material Description. This specification covers the properties of a UV stabilized, scratch resistant, pellet form, injection molded b
2、lend of polypropylene, EPDM, and mineral filler. Copyright 2003 General Motors Corporation All Rights Reserved 1.1.1 Paintability. Approved paint systems that can be used on this material are listed in the GM Approved Paint on Parts Systems (GM APOPS) database. 1.2 Symbol. The material abbreviation
3、ac- cording to ISO 11469 is E/PMD20. 1.3 Typical Application. Typical applica- tions include the following: high heat trim with good scratch resistance e.g. instrument panel trim, instrument panel substrate, rear window trim, etc. 2 References Note: Only the latest approved standards are applicable
4、unless otherwise specified. 2.1 External Standards/Specifications. ASTM D3763 ISO 75 ISO 178 ISO 294 ISO 527 ISO 1183 ISO 3451/1 ISO 11469 SAE J1545 SAE J1885 2.2 GM Standards/Specifications. GM9538P GMW3001 GMN3943 GMW3059 3 Requirements 3.1 Requirements on Delivery. Important physical, mechanical
5、and thermal properties that characterize the material are summa- rized in charts. The color shall be specified on drawings, in material specifications and otherwise. Unless otherwise specified, injection mold- ing of test specimens shall be accomplished per ISO 294. Test shall be conducted 40 h mini
6、mum after molding and immediately following a condi- tioning period of 24 h minimum in a con- trolled atmosphere of 22 3C and 50 5% RH. All tests shall be performed on unannealed specimens. Tests shall be conducted using the latest issue of the test methods indicated. Suit- able precautions should b
7、e taken to ensure that applicable safe limits are not exceeded when conducting test procedures, proc- esses, and/or handling the materials re- quired by this specification. October 2003 Originating Department: North American Engineering Standards Page 1 of 3 Copyright General Motors North America Pr
8、ovided by IHS under license with GM Licensee=IHS Employees/1111111001, User=Japan, IHS Not for Resale, 06/23/2008 23:21:46 MDTNo reproduction or networking permitted without license from IHS -,-,- GMP.E/P.119 GM ENGINEERING STANDARDS Copyright 2003 General Motors Corporation All Rights Reserved Page
9、 2 of 3 October 2003 3.1.1 Compound Properties. See Table 1. Table 1: Compound Properties (Natural) Mechanical Properties Standard Unit Values Mineral Filler ISO 3451-1, Method A % by mass 17 to 24 Density ISO 1183, Method A g/cm 1.00 to 1.08 Flexural Modulus ISO 178, 80 x 10 x 4 mm specimen, 2 mm/m
10、in test speed, 64 mm support span MPa 1700 to 2400 Tensile Stress at Yield ISO 527-1/2, specimen A, 50 mm/min test speed MPa 18 min Scratch and Mar Resis- tance GMN3943, specimen Monticello grain and dark gray color 9780 N/A Rating 1 15N with 1mm stylus and Rating of 1 20N with 7mm stylus Multiaxial
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- GMNA GMP 119 2003
链接地址:https://www.31doc.com/p-3767704.html