1、I GENERAL MOTORS ENGINEERING STANDARDS I Materials and Processes - Adhesives i ADHESIVE, INDUCTION CURE, EPOXY, STRUCTURAL - METAL 9985599 1 SCOPE. This specification details the physical proper- ties and performance requirements of a 1 component, heat curing (induction or oven), thennosetting, epox
2、y based, stnic- tural adhesive paste modified to reach sufficient handling strength (metai distortion) in a normal induction cure cycle. The adhesive is commonly used to bond steel body compo- nents such as innerlouter body panels on doors, hoods, deck lids and other components. 1.1 The adhesive sha
3、ll be a non sag material capable of adhering and bonding through ail common oils and drawing compounds approved by CPC Engineering for use on steel components. The material is compatible with piain steel (cold died), zincrometai or hot dipped and ekarocoated gaivanized steeL The adhesive m u s t be
4、homogeneous and frae of lumps or unmixed particles. The uncured material when applied in a hem fiange section must withstand production zinc phosphat- ing, - 0 processing and the subsequent bake temperames of up to W C . The adhesive can also be cured with a min 30 minute akc 1OC with or without a p
5、rior single 4 s induc- tion cum cycle in a normal, w i n coil designed fi run at 3 kHz. Other induction cure coil designs may necessitate longer dwell times for the cure cycle. The adhesive is also capable of being roboticaiiy applied in a hem flange area under n o d fabricating plant conditions. Pr
6、ovisions should be made in the fabrication process to monitor hem fiange temperatures during induction heating to insure that the level of cure nquindis met. 2 REFERENCED STANDARDS. 3.1.6 Stability. When conditioned as stated below, the adhe- sive shall be capable of meting aii the requkments of the
7、 3.1.6.1 Elevated Tempenrture Stability. The adhesive as received be capable of withstanding a temperature of 54C for 72 h without any deleterious effects. 3.1.6.2 Low Tcmpcratruie Stability. The adhesive as received shall be capable of being frozen (OC) indefinitely without any deletehms effcts on
8、the adhesive perfonnance. 3.1.7 Resmire Stability (GM9761P). The adhesive must be capable of withstanding pumping pressures without adversely effezthg its flow characttns tics. The materiai must not cake and or separak after being subjected to 13 790 kPa for 24 h . 3.1.8 Sag Characteristics (GM9749P
9、). The material shall not exhibit any perceptible slump or movement with a 6 mm dia bead applied over a n oiled, piah, steel, zincromeai, gaiva- nized or aluminum panel In addition when a 6 mm dia bead of adhesive is sandwiched between oily pieces of steel 6 mm apart, the material must not run o r f
10、low out during the produc- tion baking operation. 3.2 Material Properties (Cured State). The adhesive for the testing in t h i s section of the specification should be applied in mock up hemmed panels as shown in Figure 1. Adhesive bond line thickness w i l l be 0.127 to 0.254 mm. The steel used in
11、these panels should be of te various types outlined in the gen- eral description section of the standard coated with all the SpeCifiCati0I.C approved rpin design) run for 4 s min with 3 LHZ power. (Unless otherwise noted, the strength and performance quire- ments of the adhesive in this standard are
12、 determined w i t h Oniy an induction cure.) ASTMD1002 should be cured inan induction cure kd with 2 direct GM921P GM9751P GM9505P GM9761P SAE J243 GM951 1P 9984Ooo GM9749P ASTM D638 3 REQUIREMENB. 3.1 Ropcrtics. 3.1.1 Color. To be detexmimi a t t i m e of approval. 3.1.2 Odor. The adhesive must not
13、 have a toxic or noxious odor and shal not have any adverse effects on personnel hau- dling it. There must also be no perceptible odor from the adhesive during or aftcr cure. 3.1.3 Solids Content (ASTM D 1 0 8 4 ) 98% by mass min 3.21 Phosphate Resistance. Coat 3 sets of hem simulated panels outline
14、d in P i p 1 (0.75 mm metai gauge) made from CRS, zincrometai and galvanized with ail the currently used fabrication plant inner/outer drawing compounds and lubri- cants (30 m4m2). Apply beads of adhesive (4 to 6 mm) in the hem flange area of the panels and then induction cure as speci- fiid. Pass t
15、he panels hung vertically through a production cleaning and phosphating system where direct impingement of the spray occurs on the hcmmed areas. Panels a to be hung at heights representative o f top, nter and bottoms of a ved- caliy hung hood. The beads of adhesive in the hems must show excellent ph
16、osphate resistance w i t h no wash out from the panels. 3.1.4 Specific Gravity, room tempe- 1.32 f 0.05 3.15 Vicosity (GM9021P). When tested with a flowmeter at a pressure of 448 H a with 2.64 mm dia orifkc. 3.22 Solvent Resistance and Painabiiiy. Process the above described panels through a product
17、ion ELPO (LTniptlme) paint system. Mm m y show some &or m- face softening, but no cracking or loss of adhesion, bleeding or other deleterious effeds am allowed. The materiai should be compatible with ail electrodeposition primer systems shown on the 9984OOO A and B &awing. Bake temperature to be 1WC
18、 for 30 minutes. hitiak loto25 s 168 h WC: 30 s max 30 days 35C 30 s max AUGUST 1989 PAGE 1 9985599 Copyright General Motors North America Provided by IHS under license with GM Licensee=IHS Employees/1111111001, User=Japan, IHS Not for Resale, 06/23/2008 23:58:49 MDTNo reproduction or networking per
19、mitted without license from IHS -,-,- 1 GENERAL MOTORS ENGINEERING STANDARDS I Materials and Processes - Adheslves i Overlap Shear 4500 N min (or Metai De fomation) ADHESIVE, INDUCTION CURE, EPOXY, STRUCTURAL - METAL 9985599 Hemmed Section 4500 N min (or Metal Deformation) 3.2.2.1 Comsion Resistance
20、. Panels processed per 3.2.1 and 3.2.2should be exposed to the following environments for comsion resistance: 6 weeks GM9505P 2 0 cycles of the Scab Corrosion Enwonmcnt (GM9511P) Overiap Shear 2450 N min 23C (or Metal Defonnatiod 3.2.2.1.1 After exposure is complete, the hems should be peeled back o
21、n the test panel with the enclosed surfaces show- ing no sign of red comsion products. 3.3 PHYSICAL PROPERTES (CURED S“E). All tests in 3.3.3 and 3.3.4 should be p e r f o d on panels of the same construction as outlined in 3.2of this standard. (Unless otherwise stated these pads should only be indu
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- GMNA 9985599 1989
链接地址:https://www.31doc.com/p-3769437.html