ISO-16220-AMD-1-2007.pdf
《ISO-16220-AMD-1-2007.pdf》由会员分享,可在线阅读,更多相关《ISO-16220-AMD-1-2007.pdf(10页珍藏版)》请在三一文库上搜索。
1、 Reference number ISO 16220:2005/Amd.1:2007(E) ISO 2007 INTERNATIONAL STANDARD ISO 16220 Second edition 2005-03-01 AMENDMENT 1 2007-06-01 Magnesium and magnesium alloys Magnesium alloy ingots and castings AMENDMENT 1: Additional alloys Magnsium et alliages de magnsium Lingots et pices moules en alli
2、age de magnsium AMENDEMENT 1: Alliages supplmentaires ISO 16220:2005/Amd.1:2007(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed
3、to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the so
4、ftware products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it
5、 is found, please inform the Central Secretariat at the address given below. COPYRIGHT PROTECTED DOCUMENT ISO 2007 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying
6、and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland
7、ii ISO 2007 All rights reserved ISO 16220:2005/Amd.1:2007(E) ISO 2007 All rights reserved iii Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carrie
8、d out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. IS
9、O collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare Internatio
10、nal Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the ele
11、ments of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Amendment 1 to ISO 16220:2005 was prepared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee SC 5, Magnesium and alloys of cast or
12、wrought magnesium. ISO 16220:2005/Amd.1:2007(E) iv ISO 2007 All rights reserved Introduction The purpose of ISO 16220:2005/Amd.1:2007 is to include two new commercial alloys based on the combination of rare earth metals, gadolinium and zirconium as alloying elements. ISO 16220:2005/Amd.1:2007(E) ISO
13、 2007 All rights reserved 1 Magnesium and magnesium alloys Magnesium alloy ingots and castings AMENDMENT 1: Additional alloys Page 5, Table 1 Chemical composition of magnesium alloy ingots Replace the existing Table 1 with the following new Table 1, where two new grades are added: ISO-MgAl4RE4 and I
14、SO-MgRE3Gd1Zr. NOTE 1 The new grades ISO-MgAl4RE4 and ISO-MgRE3Gd1Zr are not included in EN 1753. Page 6, Table 2 Chemical composition of magnesium alloy castings Replace the existing Table 2 with the following new Table 2, where two new grades are added: ISO-MgAl4RE4 and ISO-MgRE3Gd1Zr. NOTE 2 The
15、new grades ISO-MgAl4RE4 and ISO-MgRE3Gd1Zr are not included in EN 1753. Page 7, Table 3 Mechanical properties of sand-cast magnesium alloys Replace the existing Table 3 with the following new Table 3, where the new grade ISO-MgRE3Gd1Zr is added at the bottom of the table. NOTE 3 The new grade ISO-Mg
16、RE3Gd1Zr is not included in EN 1753. Page 7, Table 4 Mechanical properties of permanent-mould cast magnesium alloys Replace the existing Table 4 with the following new Table 4, where the new grade ISO-MgRE3Gd1Zr is added at the bottom of the table. NOTE 4 The new grade ISO-MgRE3Gd1Zr is not included
17、 in EN 1753. Page 8, Table 5 Mechanical properties of pressure die cast magnesium alloys Replace the existing Table 5 with the following new Table 5, where the new grade ISO-MgAl4RE4 is added. NOTE 5 The new grade ISO-MgAl4RE4 is not included in EN 1753. -,-,- Table 1 Chemical composition of magnesi
18、um alloy ingots Material designation Composition % by mass Alloy group In accordance with ISO 2092:1981 a In accordance with EN 1753 Min. or max. Mg Al Zn Mn b RE c Zr Ag Y Gd Li Si Fe Cu Ni Others each RE/Al ratio ISO-MgAl9Zn1 (A) ISO-MB21120 min. max. Rem. 8,5 9,5 0,45 0,9 0,17 0,40 - - - - - - -
19、- - - - - - 0,08 - 0,004 - 0,025 - 0,001 - 0,01 - - MgAlZn ISO-MgAl9Zn1 (B) ISO-MB21121 min. max. Rem. 8,0 10,0 0,3 1,0 0,1 0,50 - - - - - - - - - - - - - 0,3 - 0,03 - 0,20 - 0,01 - 0,05 - - ISO-MgAl2Mn ISO-MB21210 min. max. Rem. 1,7 2,5 - 0,20 0,35 0,60 - - - - - - - - - - - - - 0,05 - 0,004 - 0,00
20、8 - 0,001 - 0,01 - - ISO-MgAl5Mn ISO-MB21220 min. max. Rem. 4,5 5,3 - 0,30 0,28 0,50 - - - - - - - - - - - - - 0,08 - 0,004 - 0,008 - 0,001 - 0,01 - - MgAlMn ISO-MgAl6Mn ISO-MB21230 min. max. Rem. 5,6 6,4 - 0,30 0,26 0,50 - - - - - - - - - - - - - 0,08 - 0,004 - 0,008 - 0,001 - 0,01 - - ISO-MgAl2Si
21、ISO-MB21310 min. max. Rem. 1,9 2,5 - 0,20 0,2 0,6 - - - - - - - - - - - - 0,7 1,2 - 0,004 - 0,008 - 0,001 - 0,01 - - MgAlSi ISO-MgAl4Si ISO-MB21320 min. max. Rem. 3,7 4,8 - 0,20 0,2 0,6 - - - - - - - - - - - - 0,7 1,2 - 0,004 - 0,008 - 0,001 - 0,01 - - MgAlRE d ISO-MgAl4RE4 ISO-MB21410 min. max. Rem
22、. 3,6 4,4 - 0,20 0,15 0,50 3,6 4,6 - - - - - - - - - - - 0,08 - 0,004 - 0,008 - 0,001 - 0,01 0,9 - MgZnCu ISO-MgZn6Cu3Mn ISO-MB32110 min. max. Rem. - 0,2 5,5 6,5 0,25 0,75 - - - - - - - - - - - - - 0,20 - 0,05 2,4 3,0 - 0,01 - 0,01 - - ISO-MgZn4RE1Zr ISO-MB35110 min. max. Rem. - - 3,5 5,0 - 0,15 1,0
23、 1,75 0,1 1,0 - - - - - - - - - 0,01 - 0,01 - 0,03 - 0,005 - 0,01 - - MgZnREZr d ISO-MgRE3Zn2Zr ISO-MB65120 min. max. Rem. - - 2,0 3,0 - 0,15 2,4 4,0 0,1 1,0 - - - - - - - - - 0,01 - 0,01 - 0,03 - 0,005 - 0,01 - - ISO-MgAg2RE2Zr ISO-MB65210 min. max. Rem. - - - 0,2 - 0,15 2,0 3,0 0,1 1,0 2,0 3,0 - -
24、 - - - - - 0,01 - 0,01 - 0,03 - 0,005 - 0,01 - - MgREAgZr e ISO-MgRE2Ag1Zr ISO-MB65220 min. max. Rem. - - - 0,2 - 0,15 1,5 3,0 0,1 1,0 1,3 1,7 - - - - - - - 0,01 - 0,01 0,05 0,10 - 0,005 - 0,01 - - ISO-MgY5RE4Zr ISO-MB95310 min. max. Rem. - - - 0,20 - 0,15 2,0 4,0 0,1 1,0 - - 4,75 5,5 - - - 0,20 - 0
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ISO 16220 AMD 2007
链接地址:https://www.31doc.com/p-3776157.html