1、INTERNATIONAL STANDARD IS0 14676 First edition 1997-07-I 5 Adhesives - Evaluation of the effectiveness of surface treatment techniques for alumitiium - Wet-peel test by floating-roller method Adh a=4OOnet; p=iso; o=isocs; s=central Printed in Switzerland ii Copyright International Organization for S
2、tandardization Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/23/2007 19:51:34 MDTNo reproduction or networking permitted without license from IHS -,-,- 0 IS0 IS0 14676: 1997(E) Introduction This test has been developed to assess pretreatment
3、s for aluminium and is intended for laboratory evaluations. The object was to find and develop a rapid test possessing high sensitivity which could differentiate between pickling pretreatments: complete chromic acid anodisation (CAA)/phosphoric acid anodisation (PAA) processes and incomplete ones. T
4、he application of water containing a wetting agent changes the mode of failure from cohesive failure, usually found in dry joints, to quasi-adhesive failure. The latter is associated with a corresponding reduction in the complete CAA or PAA process. The failure mechanisms in the boundary layer zone
5、initiated by this test are mainly explained by the diffusion of water. The wetting agent essentially improves the surface wetting. This test is considered to be unsuitable for long-term durability prediction. It is expected that if this severe test is applied to less stable joints it will cause main
6、ly adhesive failure. As a consequence, the test loses its ability to differentiate effectively in such circumstances. However, the applicability to other materials and surface pretreatment methods has not been investigated in detail. . . . 111 Copyright International Organization for Standardization
7、 Provided by IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/23/2007 19:51:34 MDTNo reproduction or networking permitted without license from IHS -,-,- This page intentionally left blank Copyright International Organization for Standardization Provided by
8、 IHS under license with ISO Licensee=NASA Technical Standards 1/9972545001 Not for Resale, 04/23/2007 19:51:34 MDTNo reproduction or networking permitted without license from IHS -,-,- INTERNATIONAL STANDARD o IS0 IS0 14676:1997(E) Adhesives - Evaluation of the effectiveness of surface treatment tec
9、hniques for aluminium - Wet-peel test by floating-roller method 1 Scope This International Standard is applicable to the evaluation of the quality of a surface treatment of aluminium or its alloys for high-strength adhesive bonding. 2 Normative references The following standards contain provisions w
10、hich, through reference in this text, constitute provisions of this International Standard. At the time of publication, the editions indicated were valid. All standards are subject to revision, and parties to agreements based on this International Standard are encouraged to use the most recent editi
11、ons of the standards indicated below. Members of IEC and IS0 maintain registers of currently valid International Standards. IS0 4578:-l), Adhesives - Determination of peel resistance of high-strength adhesive bonds - Floating-roller method. IS0 4588: 1995, Adhesives - Guidelines for the sueace prepa
12、ration of metals. IS0 9 142: 1990, Adhesives - Guide to the selection of standard l b) by drawing the best straight line through the peeling curve using a straight edge. Also record the maximum and minimum forces for each invidual specimen. 10 Precision The precision of this test method is not known
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ISO 14676 1997
链接地址:https://www.31doc.com/p-3776530.html