1、 Reference number ISO 22775:2004(E) ISO 2004 INTERNATIONAL STANDARD ISO 22775 First edition 2004-12-01 Footwear Test methods for accessories: Metallic accessories Corrosion resistance Chaussures Mthodes dessai pour accessoires: accessoires mtalliques Rsistance la corrosion ISO 22775:2004(E) PDF disc
2、laimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties
3、accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to t
4、he file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. ISO 2004 All r
5、ights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of
6、the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2004 All rights reserved -,-,- ISO 22775:2004(E) ISO 2004 All rights reserved iii Foreword ISO (the International
7、 Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been est
8、ablished has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardiz
9、ation. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voti
10、ng. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such
11、 patent rights. ISO 22775 was prepared by the European Committee for Standardization (CEN) in collaboration with Technical Committee ISO/TC 216, Footwear, in accordance with the Agreement on technical cooperation between ISO and CEN (Vienna Agreement). Throughout the text of this document, read “.th
12、is European Standard.” to mean “.this International Standard.”. -,-,- ISO 22775:2004(E) iv ISO 2004 All rights reserved Contents Page Forewordv 1 Scope 1 2 Terms and definitions .1 3 Principle1 4 Apparatus, materials and reagents1 5 Test specimens2 6 Conditioning.2 7 Procedure .2 7.1 Method 1 .2 7.2
13、 Method 2 .3 8 Calculation and expression of results.3 8.1 Method 1 .3 8.2 Method 2 .4 9 Test report 4 -,-,- ISO 22775:2004(E) ISO 2004 All rights reserved v Foreword This document (EN ISO 22775:2004) has been prepared by Technical Committee CEN/TC 309 “Footwear“, the secretariat of which is held by
14、 AENOR, in collaboration with Technical Committee ISO/TC 216 “Footwear“. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by June 2005, and conflicting national standards shall be withdrawn at the lat
15、est by June 2005. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland,
16、 Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. -,-,- ISO 22775:2004(E) ISO 2004 All rights reserved 1 1 Scope This document specifies two methods for determining the propensity of a metal surface
17、 to either change visually due to contamination by atmospheric pollution (Method 1: sulphide tarnishing), or to corrode due to the action of salt water (Method 2: salt water corrosion). 2 Terms and definitions For the purposes of this document, the following term and definition applies. corrosion re
18、sistance propensity of a metal surface either not to change visually due to chemical attack by atmospheric pollution, or not to be altered due to the action of salt water 3 Principle 3.1 Method 1 A test specimen is stored in a moist atmosphere containing a low concentration of hydrogen sulphide gas
19、for 1 h. The specimen is then assessed subjectively for signs of discoloration. 3.2 Method 2 Cotton lawn, saturated with sodium chloride solution, is wrapped around a test specimen. This assembly is then stored in a sealed bag for 24 h at room temperature. The test specimen is then subjectively asse
20、ssed for signs of corrosion and the lawn assessed for staining. 4 Apparatus, materials and reagents 4.1 Method 1 4.1.1 Kipps generator or other hydrogen sulphide source. WARNING This equipment should be used only by qualified personnel owing to the extremely toxicity of hydrogen sulphide. 4.1.2 Fume
21、 cupboard 4.1.3 Glass vessel which can be sealed and is of sufficient dimensions to contain the test specimen. 4.1.4 Glass tube with volume approximately equal to one thousandth of the volume of the glass vessel (4.1.3). 4.1.5 Means of suspending the test specimen in the glass vessel (4.1.3) so that
22、 the gas can circulate freely around it. NOTE Sewing thread is suitable for small test specimens; larger specimens may require plastic supports underneath. 4.2 Method 2 4.2.1 Sealable polyethylene (PE) bags of sufficient dimensions to contain the cotton lawn (4.2.2) and test specimen. ISO 22775:2004
23、(E) 2 ISO 2004 All rights reserved 4.2.2 Desized and bleached cotton lawn without finish, with an area approximately five times that of the surface area of the test specimen. NOTE Cotton lawn is a fine plain-woven fabric, made in various fine sheer qualities. 4.2.3 Sodium chloride solution of densit
24、y 30 g/dm3, sufficient quantity to fully saturate the cotton lawn (4.2.2). 5 Test specimens 5.1 Methods 1 and 2 each require two test specimens, one to be exposed to the reagents and one to be used as a reference for visually comparing any damage or discolouration of the exposed specimen. If both me
25、thods are to be carried out, then the same reference specimen can be used in both cases. If only one test component is available for each test then cut the specimen into two pieces (see NOTE). The piece containing the portion considered to be least resistant to corrosion or tarnishing should be expo
26、sed to the reagents. If cutting is impracticable record details of flaws, marks and general appearance of the test specimen prior to exposure. NOTE It is permissible to conduct this test on a part of a component provided that the part tested contains the portion of the complete component that is con
27、sidered to be least resistant to corrosion or tarnishing. This may be necessary for a number of reasons such as: Method 1: the complete component is too large to fit into the vessel (4.1.3); Method 2: the complete component is too large to fit into the bag (4.2.1). 5.2 Cut a piece of suitable dimens
28、ions from the test specimen. This piece should contain the portion considered to be least resistant to either corrosion or tarnishing. 5.3 Seal any cut edges on the portion of the component to be exposed to the reagents with epoxy resin and allow the resin to harden for at least 24 h before proceedi
29、ng with the test. 6 Conditioning The test specimens do not need to be conditioned before testing, nor does the test need to be carried out in a standard atmosphere. 7 Procedure 7.1 Method 1 7.1.1 Fill the glass tube (4.1.4) with water and pour this into the bottom of the vessel (4.1.3). 7.1.2 Seal t
30、he vessel and leave it for a minimum of 1 h to enable the humidity inside the vessel to increase and stabilise. 7.1.3 Open the vessel and put one of the test specimens inside, using the sewing thread or plastic supports (4.1.5) to suspend or support the specimen so that it is not in contact with the
31、 base of the vessel or the water. 7.1.4 Dry the glass tube fill it with hydrogen sulphide gas (4.1.1) and seal it. WARNING Hydrogen sulphide gas is very toxic and has an unpleasant smell. Extreme care should be taken not to inhale any of the gas and this test must be conducted in a fume cupboard. -,
32、-,- ISO 22775:2004(E) ISO 2004 All rights reserved 3 7.1.5 Simultaneously remove the seal from the filled glass tube and place the tube in the vessel. Immediately reseal the vessel. 7.1.6 After 60 min 5 min remove the test specimen from the vessel. 7.1.7 Place the two test specimens, one which has b
33、een exposed to hydrogen sulphide gas and one which has not, alongside each other in bright indirect lighting conditions. 7.1.8 Visually compare the two test specimens from a range of viewing angles and grade the difference according to the scale specified in 8.1. NOTE 1 The difference between a trea
34、ted and an untreated test specimen is visually assessed. NOTE 2 Assessment of the relevance of any damage or discolouration to the test specimen in this test is a very subjective process. It is therefore important to know as much as possible about the proposed application of the material and to incl
35、ude a full description of damage incurred by the test specimen in the final report. It is highly recommended that the assessment be carried out by several persons, ideally at least three persons. NOTE 3 Nickel plated articles may perform relatively poorly in this test. Severe discolouration should b
36、e ignored provided that it is uniform. 7.2 Method 2 7.2.1 Saturate the cotton lawn (4.2.2) with the sodium chloride solution (4.2.3) at room temperature. 7.2.2 Loosely wrap one of the test specimens in the wet cotton lawn ensuring that the contact area between the lawn and specimen is maximised. 7.2
37、.3 Place the test specimen and cotton lawn assembly into the bag (4.2.1). Seal the bag without expelling the air from inside so that it is partially inflated. 7.2.4 Store the bag and assembly for 24 h 1 h at room temperature. Then remove the assembly from the bag and take the test specimen out of th
38、e cotton lawn. 7.2.5 Fully rinse the test specimen and the cotton lawn in running tap water and allow them both to dry. 7.2.6 Place the cotton lawn and the two test specimens, one which has been exposed to salt water and one which has not, alongside each other in bright indirect lighting conditions.
39、 7.2.7 Visually compare (see NOTE in 7.1.8) the two test specimens from a range of viewing angles and grade the difference according to the scale specified in 8.2. Record also any staining of the cotton lawn. It is highly recommended that the assessment be carried out by several persons, ideally at
40、least three persons. 8 Calculation and expression of results 8.1 Method 1 The following scale shall be used to grade the difference between the test specimen exposed to hydrogen sulphide gas and the non exposed one: 5 No change 4 Slight uniform change 3 Slight patchy change 2 Marked change -,-,- ISO
41、 22775:2004(E) 4 ISO 2004 All rights reserved 1 Very marked change 8.2 Method 2 The following scale shall be used to grade the difference between the test specimen exposed to salt water and the non exposed one: 5 No change 4 Slight uniform change 3 Slight patchy change or slight rusting 2 Marked cha
42、nge or noticeable rusting 1 Very marked change, discolouration or rusting 9 Test report The test report shall include the following information: a) reference to this document, EN ISO 22775; b) test method (Method 1: sulphide tarnishing or Method 2: salt water corrosion) used; c) full description of
43、the test specimen and its composition, including commercial codes, colours, nature, etc.; d) amount of discolouration or corrosion as grade in 8.1 or 8.2 and number of people who carried out the assessment; e) for Method 2, any staining of the cotton lawn; f) any deviation from this test method and any incident which could affect the result; g) date of testing. -,-,- ISO 22775:2004(E) ICS 61.060 Price based on 4 pages ISO 2004 All rights reserved