《FORD-WSE-M1C180-B-2004.pdf》由会员分享,可在线阅读,更多相关《FORD-WSE-M1C180-B-2004.pdf(5页珍藏版)》请在三一文库上搜索。
1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2004 02 27 Revised Para 3.0 inserted; para 3.1 revised, 3.2, 3.3, 3.5, 4 deleted 1999 08 09 Revised Rev. Para 5.2; Complete Update M. Riley 1992 01 13 NE01E10127076035 Released R. Romano Printed copies are uncontrolled Copyright 2004, Ford Gl
2、obal Technologies, LLC Page 1 of 5 GREASE, POLYUREA, NLGI GRADE 2 WSE-M1C180-B 1. SCOPE The material defined by this specification is a NLGI 2 grease consisting of a uniform blend of refined mineral oil, a moisture resistant, polyurea compound, and rust and oxidation inhibitor. 2. APPLICATION This s
3、pecification was released originally for grease used in lubricating engine drive belt tensioner assemblies and water pump bearings. This material is designed for high speed, high temperature operation of ball and roller bearings. The operating temperature for this material is - 29 to 177 oC. 3. REQU
4、IREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Materials suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.1 Initial Qualifications Supplier must furnish to the affected Materials Engineering activity a complet
5、ed and certified copy of the attached Supplement A and test reports demonstrating full compliance with all the detailed requirements of this specification. 3.1.2 Control Plan Supplier and affected Materials Engineering activity shall establish mutually agreed upon quality control limits, which will
6、be listed on Supplement B, and will be used for ongoing product verifications at mutually agreed upon frequencies. 3.4 CONSISTENCY Material shall be a smooth homogeneous product free from abrasive particles, it shall be consistent in color and texture, and free from objectionable odors during normal
7、 storage. It shall be suitable for the intended application. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 Supplement C is to be used for additional information required for initial qualification
8、. ENGINEERING MATERIAL SPECIFICATION WSE-M1C180-B Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 5 5.2 PENETRATION (ASTM D 217) Unworked 170 - 225 After 60 strokes 265 - 295 After 100,000 strokes 380 Max (FTM 791-313) 5.3 DROPPING POINT, Min 218 oC (ASTM D 56
9、6) 5.4 OXIDATION STABILITY, Max. 34 kPa (ASTM D 942, 100 h) 5.5 OIL SEPARATION, Max 5.0% (ASTM D 1742) 5.6 COLOR Green 5.7 HIGH SPEED BEARING TEST, Min. 400 h (ASTM D 3336 at 177 oC) 5.8 CORROSION (ASTM D 1743, 24 h) 5.8.1 5% Syn Sea Water Pass 5.9 LOW TEMPERATURE TORQUE (ASTM D 1478, -18 C) 5.9.1 S
10、tarting Torque, Max 5000 g-cm 5.9.2 Running Torque, Max 1000 g-cm 5.10 RUBBER SWELL, Max 10 Vol % (ASTM D 4289, NBR-L) 5.11 STORAGE STABILITY, 38 oC, Min 6 Months 5.11.1 Penetration (ASTM D 217) After 60 strokes 265 - 295 ENGINEERING MATERIAL SPECIFICATION WSE-M1C180-B Printed copies are uncontrolle
11、d Copyright 2004, Ford Global Technologies, LLC Page 3 of 5 Supplement A Supplier _Date_ Product Name_ NLGI Grade_ Product Code_ Batch No _ Manufacturing Plant Location_ Physical/Chemical/Performance Properties Manufacturing Test Limits Results Base Oil Viscosity at 100 oC mm2/s ASTM D 445 _ _ Visco
12、sity at 40 oC mm2/s ASTM D 445 _ _ Viscosity at -40 oC mPa.s ASTM D 2983 _ _ Viscosity Index ASTM D 2270 _ _ Flash Point, oC ASTM D 92/IP 36/84 _ _ Pour Point, oC ASTM D 97 _ _ Specific Gravity ASTM D 1298 _ _ ASTM D 4052 _ _ Grease _ _ Penetration, 1/10mm ASTM D 217 _ _ Worked after 60 strokes _ _
13、Worked after 100,000 strokes FTM 791-313 _ _ Moisture Content, % ASTM D 95 _ _ Soap Content, % FLTM AJ 106-02 _ _ Water Washout at 38 oC, % ASTM D 1264 _ _ Dropping Point, oC ASTM D 556 _ _ Oxidation Stability, Kpa FLTM BJ 113-02 _ _ Pressure Drop after 500 H _ _ Oil Separation, % ASTM D 1742 _ _ Co
14、pper Strip Corrosion ASTM D 4048 _ _ Specific Gravity ASTM D 4052 _ _ Four Ball OK Load, Kgs. ASTM D 2266 _ _ Corrosion IP 220 (DIN 51802) _ _ Refractive Index ASTM D 1218 _ _ Evaporation,24 H,150 oC,Wt. - % ASTM D 972 _ _ Others (Elementals, etc.) _ _ (1) Karl Fischer (2) ASTM test method is specif
15、ic to hydrocarbon liquids at 20 to 30 oC. Signature_ Title_ MATERIAL ENGINEERING CONCURRENCE:_ ENGINEERING MATERIAL SPECIFICATION WSE-M1C180-B Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 4 of 5 Supplement B Supplier_Date_ Product Name_ NLGI Grade_ Product Code_
16、 Batch No _ Manufacturing Plant Location_ Physical/Chemical/Performance Properties Approved Approved Limits Frequency Penetration after, ASTM D 217 _ _ 60 strokes _ _ 100,000 strokes FTM 791-313 _ _ Four Ball, OK load ASTM D 2266 _ _ Timken, OK load ASTM D 2509 _ _ Wheel Bearing Leakage ASTM D 1263
17、mod. _ _ Oil Separation ASTM D 1742 _ _ Dropping Point ASTM D 566 _ _ Oxidation Stability (Pressure Drop after 100 Hrs.) ASTM D 942 _ _ Water Washout at, ASTM D 1264 _ _ At 38 oC _ _ At 80 oC _ _ Corrosion IP 220 (DIN 51802) _ _ Low Temperature Properties _ _ Low Temperature Torque IP 186 _ _ At -30
18、 oC _ _ Or Flow Pressure at -30 oC DIN 51805 _ _ Remarks_ _ SUPPLIER SIGNATURE:_ TITLE:_ MATERIAL ENGINEERING CONCURRENCE:_ ENGINEERING MATERIAL SPECIFICATION WSE-M1C180-B Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 5 of 5 Supplement C Supplier_Date_ Product Na
19、me_ NLGI Grade_ Product Code_ Manufacturing Plant Location_ BASE OIL Manufacturing Limits Nominal Viscosity Range, mm2/s Type Vol. % 100 oC 40 oC A _ _ _ _ B _ _ _ _ C _ _ _ _ D _ _ _ _ Thickener Filler/Structure Modifier/Solid Lubricant Supplier Type/Function Name Code Description A _ _ _ _ B _ _ _ _ C _ _ _ _ D _ _ _ _ E _ _ _ _ Additives Carrier/ Additive Type/ Supplier Supplier Type in final Function Name Code Description % Product % A _ _ _ _ _ _ B _ _ _ _ _ _ C _ _ _ _ _ _ D _ _ _ _ _ _ E _ _ _ _ _ _ Signature_ Title_ -,-,-